Influence of Mong Duong fly ash on the physical properties of dry pressed ceramic tiles

Minh Vu Thi Ngoc, Vo Mai Van, Tung Cao Tho, Phuong Nguyen Thi Hong, Tung Vu Hoang

Abstract


Although fly ash is a solid waste of coal-fired power plants, it is also a potential raw material for the building materials industry. In the present work, the fly ash collected from Mong Duong I power plant was characterized and used as a substitute for kaolin and feldspar at sixteen percent of a ceramic tile raw mix. The results show that fly ash promotes sintering and helps upgrade wall tiles from unsatisfactory to grade BIIa and floor tiles from grade BIII to grade BIb. These changes have significant economic and environmental implications. However, due to a relatively high firing shrinkage, it is necessary to have appropriate adjustments if applied in industrial production.

Keywords


Fly ash; feldspar; dry pressed ceramic tiles

Full Text:

PDF

References


A.N. Scott, M.D.A. Thomas, ACI Materials J. Am. Concr. Inst. 104 (2007) 62-69.

W.J. Halstead, National Cooperative Highway Research Program. 127 (1986).

N.T. Katarina Mirkovic, Goran Mladenovic, Adv. Civ. Eng. 2019 (2019). https://doi.org/10.1155/2019/8107264

Z. Nalbantoglu, Constr. Build. Mater. 18 (2004) 377-381. https://doi.org/10.1016/j.conbuildmat.2004.03.011

N.T. Liêm, Nghiên cứu tận dụng tro xỉ than nhiệt điện và cốt liệu thủy tinh để sản xuất gạch không nung, Trường Đại học Bách khoa-Đại học Đà Nẵng, 2018.

S.A. Lianyang Zhang, Jinhong Zhang, Constr. Build. Mater. 25 (2011) 3773-3781. https://doi.org/10.1016/j.conbuildmat.2011.04.005

J.X. Xing-hua Qin, Yu Feng, Arash Tahmasebi, Jiang-long Yu, Adv. Mat. Res. 1010-1012 (2014) 943-946. https://doi.org/10.4028/www.scientific.net/AMR.1010-1012.943

M. Sutcu, E. Erdogmus, O. Gencel, A. Gholampour, E. Atan, T. Ozbakkaloglu, J. Clean. Prod. 233 (2019) 753-764. https://doi.org/10.1016/j.jclepro.2019.06.017

M.-I.M. Chou, V. Patel, C.J. Laird, K.K. Ho, Energy Sources 23 (2001) 665-673. https://doi.org/10.1080/00908310119850

G. Cultrone, E. Sebastián, Constr. Build. Mater. 23 (2009) 1178-1184. https://doi.org/10.1016/j.conbuildmat.2008.07.001

H.T. Trang, Nghiên cứu khả năng sử dụng tro bay nhiệt điện trong sản xuất gạch gốm ốp lát, Trường đại học Xây dựng, 2017.

A. Zimmer, C. Bergmann, Waste Manag. 27 (2007) 59-68. https://doi.org/10.1016/j.wasman.2006.01.009

Y. Luo, S. Ma, S. Zheng, C. Liu, D. Han, X. Wang, J. Alloys Compd. 732 (2018) 828-837. https://doi.org/10.1016/j.jallcom.2017.09.179

A. Sarabia, J. Sanchez, R. Ramírez, J. Phys. Conf. Ser. 1388 (2019) 012017. https://doi.org/10.1088/1742-6596/1388/1/012017

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2002).

H.Đ. Minh, N.T. Đông, Công nghệ gốm sứ Nhà xuất bản Khoa học và Kỹ thuật, 2009.

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2005).

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2005).

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2005).

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2005).

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công Nghệ (2005).

Tiêu chuẩn Việt Nam, Bộ Khoa Học Công nghệ (2007).




DOI: https://doi.org/10.51316/jca.2021.036

Refbacks

  • There are currently no refbacks.




*******

Index: Google Scholar; Crossref

---------

Vietnam Journal of Catalysis and Adsorption

Address: Room 302  |  C4-5  |  Hanoi University of Science and Technology. 1 Dai Co Viet, Hanoi.

Tel.: ‎‎‎+84. 967.117.098 (Dr. Phượng)  |  Email: editor@jca.edu.vn  |  FB: JCA.VNACA