Preparation and characterization of ordered mesoporous carbon based catalyst derived from sodium lignosunfonate for conversion of linseed oil to biokerosene

Hong Nguyen Khanh Dieu, Luong Tran Van

Abstract


The study focused on preparation and characterization of ordered mesoporous carbon based catalyst derived from sodium lignosunfonate (MSL catalyst), and its application in conversion of linseed oil to biokerosene was also briefly discussed. The preparation of the catalyst was established by condensation-evaporation method where sulfonated biochar obtained from soditum lignosulfonate, CTAB were used as precursor and template, respectively. Water solvent was gradually evaporated during the preparation yielding a gel-like mixture at the end of the process. The catalyst with ordered mesoporous structure, high acidity, and stable activity sites was applied in the conversion of linseed oil to biokerosene, and the results based on the high yield and purity of the methyl ester product illustrated the catalysts high activity and selectivity. Some techniques were applied such as SAXRD, WAXRD, FT-IR, BET-BJH, NH3-TPD and GC-MS for characterizing the catalyst and determining the composition of the linseed oil and the biokerosene.

Keywords


Natri lignosunfonat; Xúc tác cacbon hóa; Vật liệu mao quản trung bình; Trao đổi este; Biokerosen.

Full Text:

PDF

References


S. Suganuma, K. Nakajima, M. Kitano, Microporous and Mesoporous Materials 143 (2011) 443-450. https://doi.org/10.1016/j.micromeso.2011.03.028.

J. Janaun, N. Ellis, Role of silica template in the preparation of sulfonated mesoporous carbon catalysts, Applied Catalysis A: General 394 (2011) 25–31. https://doi.org/10.1016/j.apcata.2010.12.016.

M. Toda, A. Takagaki, M. Okamura, Nature, 438 (2005) 178. https://doi.org/10.1038/438178a.

Nguyễn Khánh Diệu Hồng, Nhiên liệu sạch, NXB Khoa học và Kỹ thuật Hà Nội, 2015.

L. Wagner, Biodiesel from algae oil, Mora Asscociates Ltd, 2007.

J. Singh, S. Gu, Renewable and Sustainable Energy Reviews 14(9) (2010) 2596-2610. https://doi.org/10.1016/j.rser.2010.06.014.

V. Meynen, P. Cool, E.F Vansant, Microporous and Mesoporous Materials, 125 (2009) 170 – 223. https://doi.org/10.1016/j.micromeso.2009.03.046.

M. Zhang, A. Sun, Y. Meng, L. Wang, H. Jiang, G. Li, Microporous and Mesoporous Materials 204 (2015) 210–217. https://doi.org/10.1016/j.micromeso.2014.11.027.

Z. Gao, S. Tang, X. Cui, S. Tian, M. Zhang, Fuel 140 (2015) 669–676. https://doi.org/10.1016/j.fuel.2014.10.012.

D. Song, S. An, B. Lu, Y. Guo, J. Leng, Applied Catalysis B: Environmental 179 (2015) 445–457. https://doi.org/10.1039/C6RA19116A.

R. Liu, X. Wang, X. Zhao, P. Feng, Carbon 46 (2008) 1664–1669. https://doi.org/10.1016/j.carbon.2008.07.016.

W. Shou, D. D. Gang, R. Guo, Ordered Mesoporous Carbon: Fabrication, Characterization, and Application as Adsorbents, Dekker Encyclopedia of Nanoscience and Nanotechnology, Third Edition, Taylor & Francis, 2016. http: 10.1081/E-ENN3-120053279.

C.T. Kresge, M.E. Leonowicz, W.J Roth, J.C. Vartuli, J.C. Beck, Nature 359 (1992) 710 – 712. https://doi.org/10.1038/359710a0.

D. Zhao, Y. Wan, W. Zhou, Ordered Mesoporous Materials, Wiley-VCH Verlag & Co. KGaA Boschstr. 12, 69469 Weinheim, Germany, 2013.

L. Peng, A. Philippaerts, X. Ke, J. V. Noyen, F. D. Clippel, G. V. Tendeloo, P. A. Jacobs, B. F. Sels, Catalysis Today 150 (2010) 140–146. https://doi.org/10.1016/j.cattod.2009.07.066.

F. Lin, Z. Kun, L. Xiaohong, W. Haihong, W. Peng, Chinese Journal of Catalysis 33 (2012) 114-122. https://doi.org/10.1016/S1872-2067(10)60282-3.

L. Wang, X. Dong, H. Jiang, G. Li, M. Zhang, Catalysis Communications 56 (2014) 164–167. https://doi.org/10.1016/j.catcom.2014.07.008.

K. Chaiwong, T. Kiatsiriroa, N. Vorayos, C. Thararax, Maejo International Journal of Science and Technology, 6(02) (2012) 186-195. doi: 10.14456/mijst.2012.13.

L. J. Konwar, E. Salminen, N. Kumar, Applied Catalysis B: Environmental 176-177 (2015) 20-35. https://doi.org/10.1016/j.apcatb.2015.03.005.

Nguyễn Đăng Toàn, Vũ Đỗ Hồng Dương, Nguyễn Khánh Diệu Hồng, Tạp chí Xúc tác và Hấp phụ, T2.(Nº2) (2013) 182 – 190.

H. Xu, G. Yu, X. Mu, C. Zhang, P. D. Roussel, C. Liu, B. Li, H. Wang, Industrial Crops and Products 76 (2015) 638–646. https://doi.org/10.1016/j.indcrop.2015.07.057.

H. K. D. Nguyen, H. V. Vo, T. A. T. Dang, N. T. Dinh, Chemical Papers 72(1) (2018) 119–128. https://doi.org/10.1007/s11696-017-0263-z.

H. K. D. Nguyen, H. Q. Tran, N. L. T. Nguyen, N. T. Dinh, Journal of Porous Materials 25(6) (2018) 1567–1576. https://doi.org/10.1007/s10934-018-0570-y




DOI: https://doi.org/10.51316/jca.2020.021

Refbacks

  • There are currently no refbacks.




*******

Index: Google Scholar; Crossref

---------

Vietnam Journal of Catalysis and Adsorption

Address: Room 302  |  C4-5  |  Hanoi University of Science and Technology. 1 Dai Co Viet, Hanoi.

Tel.: ‎‎‎+84. 967.117.098 (Dr. Phượng)  |  Email: editor@jca.edu.vn  |  FB: JCA.VNACA