Synthesis of magnetic material derived from rice straw by hydrothermal carbonization for removal of methylene blue

Nguyễn Ngọc Bích1,3This email address is being protected from spambots. You need JavaScript enabled to view it., Nguyễn Đình Thành2,3

1 Trung tâm Phân tích Hóa học, Đại học Đồng Tháp
2 Viện Khoa học Vật liệu Ứng dụng Thành phố Hồ Chí Minh, Viện Hàn lâm Khoa học và Công nghệ Việt Nam
3 Học viện Khoa học và Công nghệ, Viện Hàn lâm Khoa học và Công nghệ Việt Nam

Volume 8, Issue 2pp 115-120

ABSTRACT
Rice straw, an agricultural waste, was successfully converted into novel magnetic carbon composites by low temperature hydrothermal carbonization. Firstly, rice straw (RS) is pretreated with KOH aqueous solution in stainless-steel autoclave that was Teflon lined and heated at 120 °C for 4 h, the resulting liquid is used to synthesize a black liquor-derived porous carbon. Then, magnetic carbon (MC) is carbonized at 180 °C for 14 h by the hydrothermal method. The obtained samples had a high magnetization (28,1 emu/g) and good adsorption capacity for methylene blue (MB) (qmax = 104,17 mg/g), which promised to become a potential adsorbent.

PDF Preview

Liên kết Website

Viện Kỹ thuật Hóa họcHội hóa học Việt NamTập đoàn Dầu khí Quốc gia Việt NamHội đồng chức danh Giáo sư Nhà nướcAmerican Chemical SocietyScienceDirectSpringerWiley Online LibraryOlympic Hóa học sinh viên Toàn quốc 2018
Home FIND ISSUES Online First Articles ISSUE Archives 2019 vol8-issue2-2019 Synthesis of magnetic material derived from rice straw by hydrothermal carbonization for removal of methylene blue